Sintesis dan karakterisasi Titanium Dioksida (TiO2) anatas terdoping Vanadium (V) menggunakan metode reaksi padatan

Mustofa, Khusnan (2014) Sintesis dan karakterisasi Titanium Dioksida (TiO2) anatas terdoping Vanadium (V) menggunakan metode reaksi padatan. Undergraduate thesis, Universitas Islam Negeri Maulana Malik Ibrahim.

[img]
Preview
Text (Fulltext)
09630038.pdf - Accepted Version
Available under License Creative Commons Attribution Non-commercial No Derivatives.

Download (3MB) | Preview

Abstract

INDONESIA:

Aktifitas TiO2 anatas perlu ditingkatkan dari daerah sinar UV ke daerah sinar tampak untuk meningkatkan aktifitas fotokatalis TiO2 anatas. Salah satu upaya untuk meningkatkan aktifitas fotokatalis TiO2 anatas tersebut adalah dengan doping mengunakan dopan vanadium (V). Penelitian ini bertujuan untuk mengetahui pengaruh penambahan dopan vanadium (V) terhadap struktur, ukuran kristal, energi band gap dan serapan panjang gelombang TiO2 Anatas.

Metode sintesis yang digunakan dalam penelitian ini adalah metode reaksi padatan. Tahapan yang dilakukan dalam metode ini meliputi penggerusan dan pemanasan pada suhu tinggi. Konsentrasi dopan vanadium (V) yang digunakan dalam penelitian adalah 0,3%, 0,5% dan 0,7% dan karakterisasi yang digunakan adalah difraksi sinar-X dan UV-Vis Diffuse Reflectance Spectroscopy.

Hasil dari penelitian ini menunjukkan bahwa terjadi perubahan terhadap ukuran kristal, energi band gap dan serapan panjang gelombang TiO2 anatas akibat penambaan dopan vanadium (V). Sedangkan struktur TiO2 anatas tidak mengalami perubahan. Ukuran kristal masing-masing TiO2 tanpa doping, V-TiO2 0,3%, 0,5% dan 0,7% adalah sebesar 53.21 nm, 47,67 nm, 79,65 nm dan 68,99 nm. Energi band gap masing-masing TiO2 tanpa doping, V-TiO2 0,3%, 0,5% dan 0,7% adalah 3,309 eV, 3,279 eV, 3,270 eV dam 3,259 eV. Sedangkan serapan panjang gelombang masing TiO2 tanpa doping, V-TiO2 0,3%, 0,5% dan 0,7% adalah 374,9 nm, 378,4 nm, 379,5 nm dan 380,8 nm.

ENGLISH:

TiO2 Anatase activities should be increased from the UV to the visible light photocatalytic activity of TiO2 to increase anatas. One efforts to optimize TiO2 anatase activity is doping by using dopant vanadium (V). The purpose of this research is to know the effect of addition dopan vanadium (V) on the structure, the size of the crystal, the energy band gap and the absorption wavelength of TiO2 Anatase.

Synthesis method which is used in this research is a solid reaction method. The steps being taken in this methods include grinding and heating at high temperatures. Dopant concentrations of vanadium (V) which are used in the research was 0.3%, 0.5% and 0.7%. and the characterization used is X-ray diffraction and UV-Vis Diffuse Reflectance Spectroscopy.

The result shows that there are a changing of particle size, band gap energy, and absorption of TiO2 anatas wavelength because of dopan vanadium (V) addition. While TiO2’s structure does not change. The crystal sizes of each TiO2 without doping, V-TiO2 0,3%, 0,5% and 0,7% are 53.21 nm, 47.67 nm, 79.65 nm dan 68.99 nm. Band gap energy of each TiO2 without doping, V-TiO2 0,3%,
0,5% dan 0,7% are 3.309 eV, 3.279 eV, 3.270 eV and 3.259 eV. While wavelength absorption of each TiO2 without doping, V-TiO2 0,3%, 0,5% and 0,7% are 374.9 nm, 378.4 nm, 379.5 nm and 380.8 nm.

Item Type: Thesis (Undergraduate)
Supervisor: Ningsih, Rachmawati and Abidin, Munirul
Contributors:
ContributionNameEmail
UNSPECIFIEDNingsih, RachmawatiUNSPECIFIED
UNSPECIFIEDAbidin, MunirulUNSPECIFIED
Keywords: Titanium Dioksida; Vanandium (V); Difraksi Sinar-X dan UV-Vis Diffuse Reflectance Spectroscopy; Titanium Diokside; Vanandium (V); XRD and UV-Vis Diffuse Reflectance Spectroscopy
Departement: Fakultas Sains dan Teknologi > Jurusan Kimia
Depositing User: Imam Rohmanu
Date Deposited: 13 Oct 2017 14:33
Last Modified: 13 Oct 2017 14:33
URI: http://etheses.uin-malang.ac.id/id/eprint/8253

Downloads

Downloads per month over past year

Actions (login required)

View Item View Item