#NOPUBLISH# Sintesis Zeolit NaP mesopori dari kaolin dengan variasi rasio MOL SiO2/Al2O3 menggunakan metode sonikasi sebagai katalis reaksi transesterifikasi minyak jarak (Ricinus communis)

INDONESIA :

Penggunaan kaolin alam Blitar sebagai sumber silika untuk sintesis zeolit NaP mesopori telah dilakukan. Kaolin dilakukan estraksi SiO2 untuk mendapatkan material yang amorf dan reaktif. Hasil ekstraksi SiO2 selanjutnya digunakan sebagai bahan dasar sintesis zeolit NaP mesopori dengan variasi rasio molar SiO2/Al2O3 4; 4,2 dan 4,5. Zeolit hasil sintesis digunakan sebagai katalis dalam reaksi transesterifikasi minyak jarak. Sintesis zeolit NaP mesopori menggunakan metode sonikasi dengan suhu 70⁰C selama 2 jam. Zeolit NaP dikonversi ukuran porinya menjadi ukuran mesopori dengan penambahan template surfaktan cetiltrimethyl ammonium bromide (CTABr). Karakteristik kaolin, metakaolin, dan zeolit NaP mesopori pada semua variasi telah diketahui melalui analisis XRD, XRF, dan Adsorpsi Nitrogen. Hasil sintesis Zeolit NaP mesopori digunakan sebagai katalis reaksi transesterifikasi minyak jarak pada suhu 65⁰C selama 5 jam dan dikarakterisasi menggunakan GCMS. Kaolin alam Blitar mengandung kaolin dan pengotor kuarsa yang tinggi. Kemudian kaolin alam diekstraksi menjadi SiO2 yang amorft dan reaktif sehingga dapat digunakan sintesis zeolit. Zeolit NaP mesopori berhasil dilakukan yang ditandai dengan adanya puncak zeolit NaP murni pada semua variasi rasio molar SiO2/Al2O3. Zeolit P murni pada rasio SiO2/Al2O3 = 4 dikarakterisasi menggunakan adsorpsi nitrogen didapatkan luas permukaan sebesar 72,736 m2/g, tipe isoterm mesopori, dan diameter pori sebesar 2,64 nm. Zeolit hasil sintesis kemudian digunakan sebagai katalis reaksi transesterifikasi minyak jarak. Konversi minyak jarak menjadi metil ester berhasil dilakukan yaitu terdapat 2 puncak. Puncak pertama metil oleat sebesar 5,25% dan puncak kedua metil risinoleat sebesar 94,75%.

ENGLISH :

The use of Blitar natural kaolin as a silica source for the synthesis of mesoporous NaP zeolite has been carried out. Kaolin is extracted from SiO2 to obtain an amorphous and reactive material. The SiO2 extraction results were then used as a primary material for synthesizing mesoporous NaP zeolite with variations in the SiO2/Al2O3 molar ratio of 4, 4.2, and 4.5. The synthesized zeolite is used as a catalyst in the transesterification reaction of castor oil. Synthesis of mesoporous NaP zeolite using the sonication method at 70⁰C for 2 hours. The pore size of the NaP zeolite was converted to a mesopore size by adding the surfactant template cetyl trimethyl ammonium bromide (CTABr). The characteristics of kaolin, metakaolin, and mesoporous NaP zeolite in all variations have been determined through XRD, XRF, and Nitrogen Adsorption analysis. The results of the synthesis of mesoporous NaP Zeolite were used as a catalyst for the castor oil transesterification reaction at a temperature of 65⁰C for 5 hours and characterized using GCMS. Blitar natural kaolin contains high levels of kaolin and quartz impurities. Then, natural kaolin is extracted into amorphous and reactive SiO2 for zeolite synthesis. Mesoporous NaP zeolite was successfully carried out, as indicated by pure NaP zeolite peaks at all variations in the SiO2/Al2O3 molar ratio. Pure Zeolite P at a ratio of SiO2/Al2O3 = 4 was characterized using nitrogen adsorption, resulting in a surface area of 72.736 m2/g, mesoporous isotherm type, and a pore diameter of 2.64 nm. The synthesized zeolite is then used as a catalyst for the transesterification reaction of castor oil. The conversion of castor oil into methyl ester was successful. Namely, there were two peaks. The first peak of methyl oleate was 5.25%, and the second peak of methyl ricinoleate was 94.75%.

ARABIC :

تم استخدام الكاولين الطبيعي بليتار كمصدر للسيليكا لتخليق الزيوليت NaP المسامي. يتم سحب الكاولين SiO2 للحصول على مادة غير متبلورة ومتفاعلة. ثم يتم استخدام نتائج استخراج SiO2 كمادة أساسية لتخليق الزيوليت NaP المسامي مع اختلافات في النسبة المولية ل SiO2 / Al2O3 ٤ ؛ ٤،٢ و ٤،٥. يستخدم الزيوليت المركب كعامل حفاز في تفاعل الأسترة العابرة لزيت الخروع.
تخليق الزيوليت NaP المسامي باستخدام طريقة الصوتنة مع درجة حرارة ٧٠ درجة مئوية لمدة ٢ ساعة. يتم تحويل NaP الزيوليت إلى حجم المسام إلى حجم مسامي عن طريق إضافة قالب الفاعل بالسطح لبروميد الأمونيوم سيتيليتريميثيل (CTABr). عرفت خصائص الكاولين والميتاكاولين والزيوليت NaP المسامي في جميع الاختلافات من خلال تحليل XRD و XRF وامتصاص النيتروجين. تم استخدام تخليق الزيوليت NaP المسامي كمحفز لتفاعل أسترة زيت الخروع عند ٦٥ درجة مئوية لمدة ٥ ساعات وتم توصيفه باستخدام GCMS.
يحتوي الكاولين الطبيعي بليتار على الكاولين وشوائب الكوارتز العالية. ثم يتم استخراج الكاولين الطبيعي إلى SiO2 غير متبلور وتفاعلي بحيث يمكن استخدام تخليق الزيوليت. تم إجراء الزيوليت NaP المسامي بنجاح والذي تميز بوجود قمم الزيوليت NaP النقية في جميع الاختلافات في النسبة المولية ل SiO2 / Al2O3. تم وصف الزيوليت P النقي بنسبة SiO2 / Al2O3 = ٤ باستخدام امتزاز النيتروجين الذي تم الحصول عليه بمساحة سطح ٧٢،٧٣٦ م ٢ / جم، ونوع متساوي الحرارة المسامي، وقطر المسام ٢،٦٤ نانومتر. ثم يستخدم الزيوليت المركب كعامل حفاز لتفاعل الأسترة العابرة لزيت الخروع. تم تحويل زيت الخروع إلى استر الميثيل بنجاح، أي كان هناك ٢ قمم. الذروة الأولى هي ميثيل أوليات بنسبة ٥،٢٥٪ والذروة الثانية هي ميثيل ريسينوليت بنسبة ٩٤،٧٥٪.