Rahman, Saoki (2017) Sintesis dan karakterisasi fotokatalis titanium (IV) Oksida (TiO2) terdoping perak (Ag) menggunakan metode sonikasi untuk mendegradasi bakteri Escherichia coli. Undergraduate thesis, Universitas Islam Negeri Maulana Malik Ibrahim.
Text (Fulltext)
13630106.pdf - Accepted Version Available under License Creative Commons Attribution Non-commercial No Derivatives. Download (3MB) |
Abstract
INDONESIA:
Sintesis fotokatalis titanium (IV) oksida terdoping perak telah dilakukan dengan berbagai variasi konsentrasi dopan Ag 1, 3, 5, 7, dan 9%. Penelitian ini bertujuan untuk (i) mengetahui perubahan struktur dan serapan sinar TiO2 terdoping Ag pada berbagai konsentrasi, (ii) mengetahui pengaruh TiO2 terdoping Ag terhadap kemampuan mereduksi Escherichia coli. Sintesis TiO2 terdoping Ag menggunakan metode sonikasi Bath yang bekerja pada gelombang ultrasonik. Hasil sintesis dan karakterisasi menggunakan instrumen XRD, untuk mengetahui karakteristik struktur, DRS untuk mengetahui energi celah pita dan daerah serapan sinar dan EDX untuk mengetahui komposisi Ag yang berada pada TiO2. Hasil penelitian menunjukkan bahwa dengan penambahan dopan perak dengan berbagai konsentrasi tidak merubah fasa anatas menjadi fasa rutil atau brookit. Data DRS menunjukkan bahwa Ti-O2-Ag 9% memberikan penurunan nilai reflektansi dan kenaikan koefisien absorpsi optimum. Energi celah pita masing-masing sintesis TiO2 tanpa dopan dengan TiO2-Ag 1, 3, 5, 7, dan 9% adalah 3,4; 3; 3,3; 3,1; 3,25; dan 2,8 eV. Kemampuan mereduksi pada daerah UV masing-masing sintesis TiO2 tanpa dopan dengan TiO2-Ag 1, 3, 5, 7, dan 9% dengan jumlah sel bakteri hidup adalah 3,4 x 108; 2,5 x 108; 1,3 x 108; 1,7 x 108; 6,7 x 106; 3,5 x 105 cfu/mL dan persen reduksi adalah 26,08 %; 45,7 %; 71,74%; 61,76 %; 98,48 %; dan 99,78 %. Aktivitas persen reduksi yang paling optimum pada sampel TiO2¬-9% Ag.
ENGLISH:
Silver doped Titanium (IV) oxide was synthesized with various concentration Ag 1, 3, 5, 7, and 9%. This study aimed (i) to determine the structure change and light absorption Ag doped TiO2 at various concentration, (ii) to know the effect of Ag doped TiO2 on the ability to reduce Escherichia coli. The synthesized of TiO2 doped Ag used sonication bath that worked on ultrasound waves. Characterization used XRD to know the structure characteristic, DRS to know the band gap and light absorption area, and EDX to know the composition of Ag on TiO2 latice. The result showed that Ag dopant at various concentration did not transform anatase phase into rutile or brookite phase. The DRS data showed that Ti-O2-Ag 9% had an optimum decreased in reflectance value and optimum increased in absorption coefficient. The bandgap energy of undoped and Ag doped TiO2 (1-9%) were respectively 3.4; 3; 3.3; 3.1; 3.25; and 2.8 eV. Bacterial reduction activity of photocatalyst under uv iradiation had number of bacterial cells 3.4 x 108; 2.5 x 108; 1.3 x 108; 1.7 x 108; 6.7 x 106; 3.5 x 105 cfu/mL and percent reduction 26.08 %; 45.7 %; 71.74%; 61.76 %; 98.48 %; and 99.78 %. The optimum activity achieved for 9% of silver doped TiO2.
Item Type: | Thesis (Undergraduate) | |||||||||
---|---|---|---|---|---|---|---|---|---|---|
Supervisor: | Aini, Nur and Mahmudah, Rif'atul | |||||||||
Contributors: |
|
|||||||||
Keywords: | Titaniumn (IV) Dioksida; Ag konsentrasi 1; 3; 5; 7; dan 9%; Ultrasound Methode; X-Ray Difraction (XRD); Diffuse Reflectance Spectroscopy (DRS); Diffuse Reflectance Spectroscopy (EDX) Uji degradasi E. coli. | |||||||||
Departement: | Fakultas Sains dan Teknologi > Jurusan Kimia | |||||||||
Depositing User: | Arsyadillah Arsyadillah | |||||||||
Date Deposited: | 19 Apr 2018 10:06 | |||||||||
Last Modified: | 19 Apr 2018 10:06 | |||||||||
URI: | http://etheses.uin-malang.ac.id/id/eprint/10806 |
Downloads
Downloads per month over past year
Actions (login required)
View Item |