Penentuan model Isotermis Adsorpsi Senyawa Aurivillius SrBi4Ti3,95Fe0,05O15 yang diperoleh dari metode lelehan garam NaCl-KCl untuk penurunan konsentrasi Ciprofloxacin

Indonesia :

Pencemaran perairan akibat residu ciprofloxacin berpotensi memicu resistensi bakteri sehingga diperlukan metode penanganan yang efektif. Penelitian ini bertujuan mengkaji adsorpsi ciprofloxacin menggunakan senyawa Aurivillius SrBi₄Ti₃,₉₅Fe₀,₀₅O₁₅ yang disintesis melalui metode lelehan garam NaCl-KCl. Hasil karakterisasi XRD menunjukkan bahwa senyawa SrBi₄Ti₃,₉₅Fe₀,₀₅O₁₅ berhasil terbentuk sesuai data standar JCPDS No. 00-049-0973 tanpa adanya fase pengotor. Analisis SEM menunjukkan bahwa senyawa hasil sintesis memiliki morfologi plate-like dengan ukuran berkisar antara 1–2 µm. Senyawa SrBi₄Ti₃,₉₅Fe₀,₀₅O₁₅ menunjukkan kondisi adsorpsi optimum pada pH 6 dan waktu kontak 90 menit, dengan kemampuan adsorpsi sebesar 48% serta jumlah ciprofloxacin yang teradsorpsi sebesar 3,2957 ppm. Analisis isotermis menunjukkan bahwa proses adsorpsi mengikuti model Freundlich dengan nilai R² sebesar 0,9421, serta konstanta KF dan n masing-masing sebesar 0,3925 dan 0,5020, yang mengindikasikan adsorpsi berlangsung secara multilapis pada permukaan heterogen. Analisis FTIR menunjukkan munculnya pita serapan khas ciprofloxacin serta pergeseran vibrasi Ti-O pada daerah sekitar 550 cm⁻¹ setelah adsorpsi, yang mengindikasikan adanya interaksi antara ciprofloxacin dan adsorben, melibatkan lokal struktur Ti-O.

Inggris:

Pollution of waters due to ciprofloxacin residues has the potential to trigger bacterial resistance, so effective treatment methods are needed. This study aims to examine the adsorption of ciprofloxacin using the compound Aurivillius SrBi₄Ti₃,₉₅Fe₀,₀₅O₁₅ which is synthesized through the NaCl-KCl salt melting method. The results of XRD characterization showed that the compound SrBi₄Ti₃,₉₅Fe₀,₀₅O₁₅ was successfully formed according to JCPDS standard data No. 00-049-0973 without the presence of impurity phase. SEM analysis showed that the synthesized compound had a plate-like morphology with a size ranging from 1–2 μm. The optimal adsorption condition of adsorption was achieved at pH 6 with a contact time of 90 minutes, with an adsorption ability 48% and an adsorbed ciprofloxacin concentration of 3.2957 ppm. Isothermal analysis showed that the adsorption process followed the Freundlich model with an R² value of 0.9421, and the KF and n constants of 0.3925 and 0.5020 respectively, indicating that adsorption took place multilayer on heterogeneous surfaces. FTIR analysis showed the appearance of a typical absorption band of ciprofloxacin as well as a shift in Ti-O vibration in an area of about 550 cm-1 after adsorption, indicating an interaction between ciprofloxacin and adsorbents, involving the local structure of Ti-O.

Arab:

تلوث المياه الناتج عن بقايا السيبروفلوكساسين قد يؤدي إلى مقاومة البكتيريا، لذا هناك حاجة إلى طرق معالجة فعالة. تهدف هذه الدراسة إلى فحص امتصاص السيبروفلوكساسين باستخدام مركب Aurivillius SrBi₄Ti₃,₉₅Fe₀,₀₅O₁₅ الذي يتم تصنيعه بواسطة طريقة صهر الملح NaCl-KCl. أظهرت نتائج توصيف XRD أن المركب SrBi₄Ti₃,₉₅Fe₀,₀₅O₁₅ تم تشكيله بنجاح وفقا لبيانات JCPDS القياسية رقم 00-049-0973 دون وجود طور الشوائب. أظهر تحليل SEM أن المركب المصطنع كان له شكل يشبه الصفيحة بحجم يتراوح بين 1–2 ميكرومتر. تم تحقيق الحالة المثلى للامتصاص عند درجة حموضة 6 مع وقت اتصال 90 دقيقة، مع قدرة امتصاص 32٪. أظهر التحليل المتساوي الحراري أن عملية الامتزاز اتبعت نموذج فريندليش بقيمة R² 0.9421، وثوابت KF و n بقيمة 0.3925 و0.5020 على التوالي، مما يشير إلى أن الامتصاص حدث في طبقات متعددة على أسطح غير متجانسة. أظهر تحليل FTIR ظهور شريط امتصاص نموذجي من السيبروفلوكساسين، بالإضافة إلى تحول في اهتزاز Ti-O في منطقة حوالي 550 سم-1 بعد الامتصاص، مما يشير إلى تفاعل بين السيبروفلوكساسين والممتصات، ويشمل البنية المحلية ل Ti-O.