Uji aktivitas antioksidan nanopartikel tembaga hasil green synthesis menggunakan variasi volume bioreduktor ekstrak kulit manggis (Garcinia mangostana Linn.)

Indonesia:

Nanopartikel merupakan partikel dengan ukuran yang sangat kecil yaitu 1-100 nm. Nanopartikel tembaga disintesis dengan mereduksi ion logam Cu2+ menjadi Cu0. Pada teknik sintesis nanopartikel tembaga terdapat beberapa metode sintesis yaitu top down, bottom up, dan green synthesis. Metode green synthesis paling banyak disukai karena menggunakan mikroorganisme atau tumbuhan sehingga tidak menimbulkan efek berbahaya pada lingkungan. Pada penelitian ini sintesis nanopartikel tembaga (CuNPs) menggunakan metode green synthesis dengan variasi perbandingan volume bioreduktor ekstrak kulit buah manggis (Garcinia mangostana Linn.) dan prekursor CuSO4.5H2O (0,5:1; 0,75:1; 1:1). Hasil sintesis yang terbentuk dikarakterisasi menggunakan spektrofotometer UV-Vis dan SEM-EDS (Scanning Electron Microscope-Energy Dispersive X-Ray Spectroscopy). Seluruh hasil variasi sintesis kemudian diuji aktivitas antioksidannya menggunakan metode DPPH untuk mengetahui pengaruh variasi perbandingan bioreduktor terhadap peredaman radikal bebas. Hasil UV-Vis menunjukkan puncak serapan pada 282 nm untuk variasi 0,5:1 dan 0,75:1, serta 281 nm untuk variasi 1:1, dengan absorbansi tertinggi pada variasi 1:1 sebesar 0,338. Hasil SEM menunjukkan bahwa variasi 1:1 memenuhi rentang ukuran nanopartikel dengan ukuran rata-rata 98,4 nm, sedangkan variasi 0,5:1 dan 0,75:1 memiliki ukuran rata-rata di atas 100 nm sehingga lebih tepat disebut partikel tembaga. Analisis EDS pada variasi 1:1 menunjukkan adanya unsur Cu sebagai komponen dominan sebesar 44,29%. Uji aktivitas antioksidan pada nanopartikel tembaga pada ketiga variasi sintesis (0,5:1; 0,75:1; 1:1) memiliki nilai IC50 berturut-turut sebesar 1331,55 ppm, 1096,54 ppm, dan 126,11 ppm. Berdasarkan hasil tersebut, variasi 1:1 merupakan kondisi sintesis terbaik menghasilkan absorbansi tertinggi, ukuran partikel paling kecil, distribusi lebih baik, serta aktivitas antioksidan kategori sedang terhadap DPPH.

Inggris:

Nanoparticles are very small particles with sizes of 1-100 nm. Copper nanoparticles are commonly synthesized by reducing Cu2+ metal ions to Cu0. Copper nanoparticle synthesis can be carried out using several approaches, including top-down, bottom-up, and green synthesis. Green synthesis is preferred because it uses microorganisms or plant extracts, thereby reducing hazardous environmental impacts. In this study, copper nanoparticles (CuNPs) were synthesized through green synthesis using variations in the volume ratio of mangosteen peel extract (Garcinia mangostana Linn.) bioreductant and CuSO4.5H2O precursor (0.5:1; 0.75:1; and 1:1). The synthesized products were characterized using UV-Vis spectrophotometry and SEM-EDS (Scanning Electron Microscopy-Energy Dispersive X-Ray Spectroscopy). All synthesis variations were tested for antioxidant activity using the DPPH method to determine the effect of bioreductant ratio on free-radical scavenging. UV-Vis spectra showed absorption peaks at 282 nm for the 0.5:1 and 0.75:1 variations and at 281 nm for the 1:1 variation, with the highest absorbance of 0.338 in the 1:1 variation. SEM analysis showed that the 1:1 variation met the nanoparticle size range, with an average particle size of 98.4 nm, whereas the 0.5:1 and 0.75:1 variations had average sizes above 100 nm and are therefore more appropriately described as copper-based particles. EDS analysis of the 1:1 variation confirmed Cu as the dominant element at 44.29%. The antioxidant activity test of the three synthesis variations (0.5:1; 0.75:1; and 1:1) produced IC50 values of 1331.55 ppm, 1096.54 ppm, and 126.11 ppm, respectively. These results indicate that the 1:1 variation is the best synthesis condition, producing the highest absorbance, the smallest particle size, a better size distribution, and moderate antioxidant activity against DPPH.

Arab:

ت ُع َ د ّ اجلسيمات النانوية (اننواپرتيكل) جسيمات ٍ ذاتَ أحجام ٍ صغرية ٍ جدًّا ترتاوح بني وتوجد عدة طرائق لتخليق اجلسيمات النانوية النحاسية، .(Cu⁰) إىل النحاس الفلزي (⁺Cu²) النحاسية من خًلل اختزال أيوانت النحاس الثنائية وت ُع َ د ّ طريقة غرين سينثيسيس األكثر تفضيًلا لعتمادها على الكائنات احلية الدقيقة وطريقة بوتوم أب، وطريقة غرين سينثيسيس ، منها طريقة توب داون ابستخدام طريقة (CuNPs) يف هذه الدراسة، مت ختليق اجلسيمات النانوية النحاسية . أو النبااتت، مما جيعلها صديقة ا للبيئة ول حتُدث آاثر ا ا ضارة هبا إىل .) غرين سينثيسيس مع اختًلف نسبة حجم العامل احليوي املختزل (بيوريدوكتور) من مستخلص قشور فاكهة املانغوستني (غارسينيا مانغوستاان لني ). وقد مت توصيف نواتج التخليق ابستخدام مطيافية األشعة فوق البنفسجية 1:1 ؛ 0.75:1 ؛ 0.5:1 ابلنسب ( CuSO₄·5H₂O املادة األولية بعد ذلك، خضعت مجيع العينات . (SEM-EDS) واجملهر اإللكرتوين املاسح املزود مبطيافية تشتت الطاقة لألشعة السينية (UV-Vis) واملرئية ة أتثري اختًلف نسبة العامل احليوي املختزل يف تثبيط اجلذور احلرة. وأظهرت هبدف معرف DPPH لختبار النشاط املضاد لألكسدة ابستخدام طريقة ، مع 1:1 اننومرت للعينة بنسبة 281 ، وعند 0.75:1 و 0.5:1 اننومرت للعينتني بنسبة 282 قمم امتصاص عند طول موجي قدره UV-Vis نتائج حققت املدى احلجمي للجسيمات 1:1 أن العينة بنسبة SEM وأظهرت نتائج . 0.338 بلغت 1:1 تسجيل أعلى قيمة امتصاص للعينة بنسبة اننومرت، مما 100 أكثر من 0.75:1 و 0.5:1 اننومرت، يف حني بلغ متوسط حجم اجلسيمات يف العينتني بنسبة 98.4 النانوية مبتوسط حجم بلغ بوصفه (Cu) وجود عنصر النحاس 1:1 للعينة بنسبة EDS جيعل تسميتها جسيمات حناسية أكثر دقة من تسميتها جسيمات اننوية. كما بنيّ حتليل ؛ 0.75:1 ؛ 0.5:1 أما نتائج اختبار النشاط املضاد لألكسدة للجسيمات النانوية النحاسية يف مجيع نسب التخليق ( .% 44.29 املكو ّ ن الرئيس بنسبة جزء ا ا يف املليون. 126.11 جزء ا ا يف املليون، و 1096.54 )، و ppm جزء ا ا يف املليون ( 1331.55 بلغت على التوايل IC₅₀ )، فقد أظهرت قيم 1:1 أفضل ظروف التخليق، إذ أعطت أعلى قيمة امتصاص، وأصغر حجم للجسيمات، وتوزيع ا ا أكثر جتانس ا ا، 1:1 واستناد ا ا إىل هذه النتائج، ت ُع َ د ّ النسبة . DPPH إضافة ا إىل نشاط ٍ مضاد ٍ لألكسدة ضمن الفئة املتوسطة جتاه مركب