Zahro, Álifatuz (2014) Sintesis dan karakterisasi Zeolit Y dari abu ampas tebu variasi rasio Molar SiO2/Al2O3 dengan metode Sol Gel Hidrotermal. Undergraduate thesis, Universitas Islam Negeri Maulana Malik Ibrahim.
![]() |
Text (Fulltext)
10630080.pdf - Accepted Version Available under License Creative Commons Attribution Non-commercial No Derivatives. Download (4MB) |
Abstract
INDONESIA:
Abu ampas tebu mengandung kadar silika (SiO2) yang tinggi. Silika yang tinggi dapat digunakan sebagai komponen utama sintesis zeolit selain alumina, salah satunya adalah zeolit Y. Zeolit Y merupakan zeolit sintetik jenis faujasit yang kaya akan silika dengan rentang rasio molar SiO2/Al2O3 1,5-3 dengan bentuk struktur SBU D6R. Zeolit Y dalam skala laboratorium maupun industri banyak dimanfaatkan sebagai padatan pendukung katalis untuk reaksi hidrorengkah fraksi berat minyak bumi, bahan adsorben, maupun ion exchange (pertukaran ion). Oleh karena itu, sintesis zeolit Y perlu untuk disintesis. Tahap sintesis metode sol gel meliputi tahap pencampuran bahan sesuai rasio molar SiO2/Al2O3 2, 2,5 dan 3 dengan komposisi molar 15SiO2 : 1,0Al2O3 : 10Na2O : 300H2O, distirer selama 30 menit dan dieramkan selama 30 menit, dilanjutkan dengan hidrotermal pada suhu 100 ºC selama 24 jam dan tahap yang terakhir adalah pengeringan zeolit Y pada suhu 100ºC selama 12 jam. Hasil sintesis dikarakterisasi menggunakan XRF, XRD, FTIR, dan uji luas permukaan dengan metode adsorpsi methylene blue. Analisis XRF menunjukkan bahwa silika abu ampas tebu sebesar 44,6%. Analisis XRD menunjukkan hasil sintesis menghasilkan campuran zeolit Y dan P, kristalinitas zeolit Y rasio SiO2/Al2O3 3 > rasio SiO2/Al2O3 2,5 > rasio SiO2/Al2O3 2. Analisis pendukung dengan FTIR menunjukkan puncak-puncak yang muncul pada ketiga rasio zeolit Y merupakan gugus fungsi terbentuknya kerangka zeolit Y. Luas permukaan zeolit Y dengan adsorpsi methylene blue rasio SiO2/Al2O3 2, 2,5 dan 3 berturut-turut adalah sebagai berikut 15,0914 m2/gram, 15,0805 m2/gram, dan 15,1747 m2/gram
ENGLISH:
Bagasse ash contains high level of silica (SiO2). Silica is one of two principal raw materials to manufacture zeolite, such as zeolite Y. Zeolite Y is synthetic faujasite-type zeolite which has high level of silica with SiO2/Al2O3 molar ratio 1,5-3 and its structure is built by secondary building unit D6R. In laboratory and industry, zeolite Y is used as catalyst support for hydrocracking of heavy petroleum fractions reaction, adsorbent, and ion exchange agent, therefore, synthesis of zeolite Y is needed. Variation of SiO2/Al2O3 molar ratio are 2 ; 2,5 and 3. Materials were mixed with composition 15SiO2 : 1,0Al2O3 : 10Na2O : 300H2O and stirred for 30 minutes. After that, the mixture was allowed to stand for 30 minutes and then it was given hydrothermal treatment at 100 oC for 24 hours. The hydrothermal result was dried at 100 oC for 12 hours. Synthesized materials are characterized by XRF, XRD and FTIR. The surface area analysis was conducted with methylene blue adsorption. The result of XRF showed that the percentage of silica content in bagasse ash was 44,6 %. XRD exhibited two kinds of zeolite, zeolite Y and P, were formed. The result of FTIR confirmed about the formation of zeolites by peaks that appeared were the characteristic functional group of zeolite Y framework. The crystallinity of zeolite Y with SiO2/Al2O3 molar ratio 3 > 2,5 > 2. The surface area of zeolite Y with SiO2/Al2O3 molar ratio 2, 2,5 and 3 were 15.0914 m2/gram, 15.0805 m2/gram, and 15.1747 m2/gram.
Item Type: | Thesis (Undergraduate) | |||||||||
---|---|---|---|---|---|---|---|---|---|---|
Supervisor: | Amalia, Suci and Adi, Tri Kustono | |||||||||
Contributors: |
|
|||||||||
Keywords: | Abu ampas tebu; zeolit Y; metode sol gel hidotermal; Bagasse ash | |||||||||
Departement: | Fakultas Sains dan Teknologi > Jurusan Kimia | |||||||||
Depositing User: | Heni Kurnia Ningsih | |||||||||
Date Deposited: | 12 Jan 2018 14:49 | |||||||||
Last Modified: | 12 Jan 2018 14:49 | |||||||||
URI: | http://etheses.uin-malang.ac.id/id/eprint/8423 |
Downloads
Downloads per month over past year
Actions (login required)
![]() |
View Item |