Fotodegradasi zat warna methylen blue menggunakan TIO2/Zeolit dengan penambahan Ion Nitrat (NO3-)

Erwanto, Erwanto (2014) Fotodegradasi zat warna methylen blue menggunakan TIO2/Zeolit dengan penambahan Ion Nitrat (NO3-). Undergraduate thesis, Universitas Islam Negeri Maulana Malik Ibrahim.

[img]
Preview
Text (Fulltext)
09630050.pdf - Accepted Version
Available under License Creative Commons Attribution Non-commercial No Derivatives.

Download (4MB) | Preview

Abstract

INDONESIA:

Methylen blue merupakan zat warna memiliki efek berbahaya untuk kesehatan manusia, karena dibuat dari senyawa azo yang mengandung gugus kromofor –N=N- dalam molekulnya. Komposit TiO2/zeolit dapat digunakan untuk mendegradasi zat pewarna. Aktivitas zeolit alam dapat ditingkatkan dengan aktivasi dan pengembanan TiO2. Tujuan penelitian ini adalah mengetahui karakterisasi TiO2/zeolit, jumlah penambahan TiO2/zeolit efektif dan konsentrasi penambahan ion NO3- efektif serta waktu lama penyinaran efektif terhadap fotodegradasi methylen blue.

Zeolit alam diaktivasi menggunakan NH4NO3 2 M dan diperoleh H-zeolit. H-zeolit dicampur TiO2 dengan perbandingan (97:3) % dengan metode hidrotermal dan kalsinasi pada suhu 500 selama 4 jam. Karakterisasi komposit TiO2/zeolit dengan XRD. Dilakukan variasi penambahan komposit dalam proses fotodegradasi tehadap methylen blue dengan penyinaran lampu UV. Hasil terbaik variasi penambahan komposit akan ditambahkan pada variasi konsentrasi penambahan NO3 tehadap methylen blue dengan penyinaran lampu UV.

dalam proses fotodegradasi Hasil karakterisasi XRD menunjukkan zeolit alam tidak mengalami perubahan struktur, namun terjadi perubahan intensitas akibat penambahan TiO2. Penambahan komposit TiO2/zeolit terbaik sebanyak 75 mg dengan efektifitas degradasi sebesar 29,94%. Dan penambahan NO3- terbaik pada konsentrasi 0,5 M dengan efektifitas degradasi sebesar 30,81 % pada penyinaran lampu UV selama 100 menit.

ENGLISH:

Methylen blue is a dye that has a harmful effect for human healt, because it is made of compounds countaining azo chromophore group –N=N- in it molecule. Composite zeolite-TiO2 can be used to degrade dye. Natural zeolite activity can be enhanced by activation and developing of TiO2. The purpose of this study is to investigate the characterization of zeolite-TiO2 , the number of effective zeolite addition and addition of effective ion concentration, and prolonged irradiation is effective against Methylen blue photodegradation.

Actived natural zeolite used NH4NO3 2 M retrieved H-zeolite, H-zeolite mixed TiO2 with ratio (97:3) % by hydrothermal method and calcinations at temperatures 500 for the four-hour. Characterization of composite zeolite- TiO2 with XRD. Did variations in the process of added composite photodegradation to methylen blue by irradiating UV light. The best resulted are variations addition of composite could be add to increase NO3- the concentration variation in the process of photodegradation to methylen blue by irradiating UV light.

The resulted of the characterization XRD of the natural zeolit showed no change structure, however, the intensity changes due to the addition of TiO2. The best addition of composite zeolit-TiO2 as much as 75 mg with the effectiveness of degradation at 29,94 % and addition the best NO3- to concentration at 0,5 M, with the effectiveness of degradation by 30,81 % at irradiated UV ligh as much as 100 minutes.

Item Type: Thesis (Undergraduate)
Supervisor: Amalia, Suci and Adi, Tri Kustono
Keywords: Zeolit Alam Malang; Komposit; TiO2; Fotodegradasi; NO3-; Natural zeolite malang; Composite; TiO2; Photodegradation; NO
Departement: Fakultas Sains dan Teknologi > Jurusan Kimia
Depositing User: Imam Rohmanu
Date Deposited: 13 Oct 2017 07:33
Last Modified: 13 Oct 2017 07:33
URI: http://etheses.uin-malang.ac.id/id/eprint/8264

Actions (login required)

View Item View Item