Analisis potensi ekstrak daun Belimbing Wuluh sebagai anti korosi pada baja SS400 dalam larutan Nacl 3,5%

INDONESIA:

Korosi adalah penurunan kualitas logam akibat reaksi elektrokimia dengan lingkungan. Pada industri perkapalan, korosi merupakan kendala utama yang menyebabkan degradasi material pada pelat lambung kapal akibat interaksi berkelanjutan dengan lingkungan air laut yang agresif.

Penelitian ini bertujuan untuk menganalisis pengaruh variasi waktu ekstraksi metode MAE terhadap konsentrasi tanin daun belimbing wuluh (Averrhoa bilimbi L.) serta pengaruh lama perendaman terhadap efisiensi inhibisi korosi dan karakteristik permukaan baja SS400 yang direndam dalam larutan NaCl 3,5% dengan dan tanpa ekstrak tanin dari daun belimbing wuluh (Averrhoa bilimbi L.). Ekstraksi tanin dilakukan menggunakan Microwave Assisted Extraction (MAE) dengan variasi waktu 0,3,6,9,12 menit dan lama perendaman 7,12, dan 17 hari. Karakterisasi untuk mendapatkan kadar tanin dilakukan dengan spektrofotometer UV-Vis. Pengujian aplikasi inhibitor dilakukan dengan metode weight loss dan EIS. Selain itu, karakteristik permukaan baja akan dianalisis menggunakan mikroskop digital.

Hasil penelitian menunjukkan sampel dengan ekstraksi 6 menit memiliki kandungan tanin tertinggi sebesar 16,425 mg/L. Laju korosi terendah ditemukan pada sampel BT6 setelah perendaman 17 hari sebesar 1,2572 mm/y dengan efisiensi 83,5508%. Selain itu, uji EIS menunjukkan efisiensi sampel BT6 lebih tinggi dibandingkan BT0 dan BNaCl yaitu sebesar (88,71%). Pengamatan permukaan baja menggunakan mikroskop digital menunjukkan sampel mengalami korosi paling sedikit yaitu sampel BT6.

ENGLISH:

Corrosion is the deterioration of metal quality due to electrochemical reactions with the environment. In the shipping industry, corrosion is a major challenge that causes material degradation on ship hull plates due to continuous interaction with the aggressive seawater environment.

This study aims to analyze the effect of varying extraction times in the MAE method on the tannin concentration of bilimbi leaves (Averrhoa bilimbi L.) and the effect of soaking duration on corrosion inhibition efficiency and surface characteristics of SS400 steel soaked in 3.5% NaCl solution, with and without tannin extract from bilimbi leaves (Averrhoa bilimbi L.). Tannin extraction was carried out using Microwave Assisted Extraction (MAE) with extraction times of 0, 3, 6, 9, and 12 minutes, and soaking durations of 7, 12, and 17 days. Characterization to determine tannin content was performed using a UV-Vis spectrophotometer. The inhibitor application test was conducted using the weight loss and EIS methods. In addition, the surface characteristics of the steel were analyzed using a digital microscope.

The study results showed that the sample with a 6-minute extraction had the highest tannin content of 16.425 mg/L. The lowest corrosion rate was found in the BT6 sample after 17 days of immersion, at 1.2572 mm/y with an efficiency of 83.5508%. Furthermore, EIS testing showed that the efficiency of the BT6 sample was higher compared to BT0 and BNaCl, at 88.71%. Observation of the steel surface using a digital microscope showed that the sample experienced the least corrosion, which was the BT6 sample.

ARABIC:

التآكل هو انخفاض جودة المعادن نتيجة لتفاعل كيميائي كهربائي مع البيئة. في صناعة السفن، يمثل التآكل عقبة رئيسية تسبب تدهور المواد في صفائح هيكل السفينة بسبب التفاعل المستمر مع بيئة المياه البحرية العدوانية.

تهدف هذه الدراسة إلى تحليل تأثير اختلاف وقت الاستخلاص باستخدام طريقة MAE على تركيز الدباغ من أوراق الكرمة الحامضة (أفيروها بيليمبي ل) وكذلك تأثير مدة النقع على كفاءة تثبيط التآكل وخصائص سطح فولاذ ٤٠٠SSالمنقوع في محلول NaCl بتركيز ٣،٥٪مع وخارج مستخلص الدباغ من أوراق الكرمة الحامضة (أفيروها بيليمبي ل.). تم استخلاص الدباغ باستخدام طريقة الاستخلاص بمساعدة الميكروويف (MAE) مع تغييرات في الوقت ٠، ٣، ٦، ٩، ١٢ دقيقة وفترات النقع ٧، ٢ ١ ، و٧ ١يوماً. تم إجراء توصيف للحصول على محتوى التانين باستخدام مطياف الأشعة فوق البنفسجية-المرئية. وتم اختبار تطبيق المثبط باستخدام طريقة فقدان الوزن وتقنية قياس المقاومة الكهربائية المغمورة EIS. بالإضافة إلى ذلك، سيتم تحليل خصائص سطح الفولاذ باستخدام المجهر الرقمي.

أظهرت نتائج البحث أن العينة ذات الاستخلاص لمدة ٦ دقائق تحتوي على أعلى نسبة تانين بلغت ١٦٬٤٢٥ملغ/لتر. تم العثور على أقل معدل تآكل في العينة ٦BTبعد نقعها لمدة ١٧ يومًا بمقدار ١٫٢٥٧٢ ملم/سنة بكفاءة ٨٣٫٥٥٠٨٪.بالإضافة إلى ذلك، أظهر اختبار EIS أن كفاءة العينة ٦BTأعلى مقارنةً بـ ٠ BTوBNaCl حيث بلغت ٨٨٫٧١ ٪. وأظهر فحص سطح الفولاذ باستخدام المجهر الرقمي أن العينة٦BT شهدت أدنى معدل تآكل.