Pengolahan limbah farmasi (asam salisilat) menggunakan fotokatalitik berbasis material Ag/Fe2O3

INDONESIA:

Limbah farmasi merupakan salah satu sumber pencemaran lingkungan yang memerlukan pengolahan khusus untuk mengurangi dampak negatifnya. Penelitian ini bertujuan untuk mensintesis material Ag/Fe₂O₃ menggunakan metode hidrotermal dan fotoreduksi serta mengevaluasi pengaruh dosis katalis Ag/Fe₂O₃ terhadap degradasi asam salisilat dan campuran polutan sulfanilamid. Material hasil sintesis dikarakterisasi menggunakan instrumen XRD (X-Ray Diffraction) dan SEM (Scanning Electron Microscopy). Proses fotokatalitik dilakukan selama 1 jam dengan interval waktu 0 menit, 15 menit, 30 menit, 45 menit, dan 60 menit untuk pengambilan sampel. Uji intensitas penyinaran fotokatalisis dilakukan untuk menilai efektivitas intensitas penyinaran terhadap degradasi polutan. Hasil degradasi dianalisis menggunakan spektrofotometer UV-Vis untuk menentukan kadar dan persentase degradasi. Hasil penelitian menunjukkan bahwa material Ag/Fe₂O₃ berhasil disintesis menggunakan metode hidrotermal. Degradasi asam salisilat mencapai 13,82% dalam 60 menit dengan dosis katalis 150 mg. Pada campuran polutan, struktur kompleks polutan menghambat reaktivitas radikal hidroksil (•OH), sehingga sulfanilamid mendominasi sisa polutan yang tidak terdegradasi sempurna. Uji selektivitas menunjukkan total degradasi asam salisilat sebesar 35,23%, sedangkan sulfanilamid mencapai 31,64% dalam waktu 60 menit. Berdasarkan hasil ini, dapat disimpulkan bahwa material Ag/Fe₂O₃ efektif untuk mendegradasi asam salisilat tetapi kurang sesuai untuk degradasi sulfanilamid pada campuran polutan.

ENGLISH:

Pharmaceutical waste is one of the environmental pollutants that requires special treatment to minimize its negative impact. This study aims to synthesize Ag/Fe₂O₃ material using hydrothermal and photoreduction methods and evaluate the effect of Ag/Fe₂O₃ catalyst dosage on the degradation of salicylic acid and sulfanilamide pollutant mixtures. The synthesized material was characterized using XRD (X-Ray Diffraction) and SEM (Scanning Electron Microscopy). The photocatalytic process was conducted for 1 hour with sampling intervals at 0 minutes, 15 minutes, 30 minutes, 45 minutes, and 60 minutes. The photocatalysis irradiance intensity test was conducted to assess the effectiveness of irradiance intensity on pollutant degradation. The degradation results were analyzed using a UV-Vis spectrophotometer to determine the concentration and percentage of degradation. The results showed that the Ag/Fe₂O₃ material was successfully synthesized using the hydrothermal method. The degradation of salicylic acid reached 13.82% within 60 minutes with a catalyst dosage of 150 mg. In the pollutant mixture, the complex structure of pollutants inhibited the reactivity of hydroxyl radicals (•OH), leaving sulfanilamide as the dominant residual pollutant that was not completely degraded. Selectivity tests revealed a total degradation of 35.23% for salicylic acid and 31.64% for sulfanilamide within 60 minutes. Based on these results, it can be concluded that the Ag/Fe₂O₃ material is effective for degrading salicylic acid but less suitable for sulfanilamide degradation in pollutant mixtures.

ARAB:

تعتبر النفايات الصيدلانية من مصادر التلوث البيئي التي تتطلب معالجة خاصة لتقليل تأثيرها السلبي. استهدف هذا البحث إلى تخليق مواد Ag/Fe₂O₃ باستخدام طرق الاختزال الحراري المائي والاختزال الضوئي وتقييم تأثير جرعة محفز Ag/Fe₂O₃ على تحلل مخاليط ملوثات حمض الساليسيليك والسلفانيلاميد. تم تمييز المادة المركبة باستخدام أدوات XRD (حيود الأشعة السينية) و SEM (الفحص المجهري الإلكتروني الماسح). تم تنفيذ عملية التحفيز الضوئي لمدة ساعة واحدة بفواصل زمنية من 0 دقيقة و 15 دقيقة و 30 دقيقة و 45 دقيقة و 60 دقيقة لأخذ العينات. تم إجراء اختبارات الانتقائية على مخاليط الملوثات لتقييم فعالية المحفزات ضد كل مركب. تم تحليل نتائج التحلل باستخدام مقياس الطيف الضوئي لأشعة الشمس لتحديد درجة ونسبة التحلل. أظهرت نتيجة البحث أن مواد Ag/Fe₂O₃ قد تم تصنيعها بنجاح باستخدام الطرق الحرارية المائية. وصل تحلل حمض الساليسيليك إلى 13.82٪ في 60 دقيقة بجرعة محفزة 150 مجم. في خليط الملوثات، يمنع التركيب المعقد للملوثات تفاعل جذور الهيدروكسيل (•OH)، لذلك يهيمن السلفانيلاميد على الملوثات المتبقية التي لا تتحلل تماما. أظهر اختبار الانتقائية أن التحلل الكلي لحمض الساليسيليك كان 35.23٪، بينما وصل السلفانيلاميد إلى 31.64٪ في غضون 60 دقيقة. بناء على هذا، يمكن الاستنتاج أن مادة Ag/Fe₂O₃ فعالة في تحلل حمض الساليسيليك ولكنها أقل ملاءمة لتحلل السلفانيلاميد في مخاليط الملوثات.