Variasi penambahan komposit fotokatalis TiO2anatas-k2o/Zeolit pada reaksi transesterifikasi minyak jarak untuk pembuatan biodiesel

Alfian, Mohammad Lutfi (2017) Variasi penambahan komposit fotokatalis TiO2anatas-k2o/Zeolit pada reaksi transesterifikasi minyak jarak untuk pembuatan biodiesel. Undergraduate thesis, Universitas Islam Negeri Maulana Malik Ibrahim.

[img]
Preview
Text (Fulltext)
12630055.pdf - Accepted Version
Available under License Creative Commons Attribution Non-commercial No Derivatives.

Download (4MB) | Preview

Abstract

INDONESIA:

Biodiesel merupakan sumber energi alternatif pengganti bahan bakar fosil. Proses pembuatan biodiesel telah dilakukan melalui reaksi transesterifikasi minyak jarak dengan variasi penambahan komposit fotokatalis TiO2anatas-K2O/zeolit sebesar 10, 15 dan 20 % dari berat minyak. Sintesis komposit diawali dengan aktivasi zeolit menggunakan HCl 6 M. Kemudian dimpregnasi dengan KOH 20 %. Selanjutnya pengembanan TiO2 pada zeolit dengan metode Hidrotermal. Komposit dikarakterisasi dengan XRD dan FTIR. Munculnya puncak K2O dan TiO2 pada difaktogram XRD dan vibrasi Ti-O-Ti pada spektra FTIR menunjukkan sintesis berhasil dilakukan. Reaksi dilakukan pada suhu ruang selama 4 jam dengan perbandingan mol minyak dan metanol 1:7. Produk reaksi dianalisis dengan FTIR dan GC-MS. Hasil analisis menunjukkan bahwa kondisi terbaik penambahan komposit fotokatalis adalah 15 % dengan kadar biodiesel sebesar 66,479 %. Karakteristik biodiesel yang dihasilkan pada penambahan 15 % fotokatalis ini yaitu meliputi kadar air 2,80 %, kadar asam lemak bebas 0,107 mg-KOH/g dan densitas 0,939 g/mL.

ENGLISH:

Biodiesel is an alternative energy. The transesterification process of castor oil to methyl ester (biodiesel) was studied using composites TiO2anatas-K2O/zeolite as photocatalyst with various adding of 10,15 and 20 % weight of oil. Composites shinthesized through activation zeolite by using 6 M HCl. Continued with impregnated using 20 % of KOH. Zeolite supported on TiO2 using hydrothermal methods. The composites characterized XRD and FTIR. The peak of K2O and TiO2 was showed in diffractogram of XRD, The vibrations of Ti-O-Ti was showed in spectra FTIR, the synthesis was successful. The condition reaction at room temperature for 4 hours with the ratio between oil and methanol 1 : 7. Biodiesel analyzed FTIR and GC-MS. The analysis was showed the variation of adding composites photocatalyst is 15 % with the yield of biodiesel 66,479 %. The characteristic of biodiesel 15 % photocatalyst has value water content 2,80 %, free fatty acid 0,107 mg-KOH/g and the density 0,939 g/mL.

Item Type: Thesis (Undergraduate)
Supervisor: Amalia, Suci and Jannah, Akyunul
Keywords: TiO2anatas-K2O/zeolit; Variasi penambahan komposit; TransesterifikasiL; Minyak jarak; Biodiesel; TiO2anatase-K2O/zeolite; Variation in addition composite; Castor Oil; Transesterification; Biodiesel
Departement: Fakultas Sains dan Teknologi > Jurusan Kimia
Depositing User: Imam Rohmanu
Date Deposited: 26 Apr 2017 09:09
Last Modified: 26 Apr 2017 09:09
URI: http://etheses.uin-malang.ac.id/id/eprint/6522

Actions (login required)

View Item View Item