Sintesis dan karakterisasi nanokomposit Tio2/Zeolit alam Malang dengan variasi konsentrasi Hno3

Mahmudah, Rizqiatul (2017) Sintesis dan karakterisasi nanokomposit Tio2/Zeolit alam Malang dengan variasi konsentrasi Hno3. Undergraduate thesis, Universitas Islam Negeri Maulana Malik Ibrahim.

[img]
Preview
Text (Fulltext)
12630013.pdf - Accepted Version
Available under License Creative Commons Attribution Non-commercial No Derivatives.

Download (4MB) | Preview

Abstract

INDONESIA:

Fotokatalis nanokomposit TiO2/zeolit alam Malang telah dilakukan sintesis menggunakan metode sol-gel dengan variasi konsentrasi HNO3 0,3; 0,4; dan 0,5 M. Konsentrasi terbaik dalam pembentukan gel telah dipelajari pengaruhnya terhadap pembentukan nanokomposit. XRF, XRD, dan SEM telah digunakan untuk karakterisasi nanokomposit TiO2/zeolit alam Malang hasil sintesis. Hasil sintesis menunjukkan bahwa TiO2 berhasil terembankan pada zeolit alam Malang. Ukuran nano pada komposit juga telah dihasilkan dari semula zeolit alam berukuran sekitar 98-161 nm menjadi TiO2/zeolit alam berukuran 51-83 nm. Hasil terbaik dari variasi konsentrasi HNO3 adalah 0,3 M. Hasil SEM menunjukkan bahwa TiO2 terdistribusi pada permukaan zeolit alam Malang. Hasil SEM diperkuat dengan data XRF dari nanokomposit TiO2/zeolit alam Malang dengan kadar awal Ti sebesar 2,65 % menjadi 46,4 %.

ENGLISH:

Photocatalysts nanocomposites TiO2/zeolite nature Malang has been synthesized using sol-gel mathod with variation concentration HNO3 0,3; 0,4; dan 0,5 M. The best concentration in gel formation have been used for the characterization of nanocomposites TiO2/zeolite synthesized. The results showed that the synthesis of TiO2 successfully dopped on nature zeolite of Malang. the size of the nanocomposites have also composites have also been produced from the original nature zeolite measurmed about 98-161 nm into TiO2/zeolite size of 51-83 nm. The best results from the variation of consentration HNO3 is 0,3 M.The result of SEM indicates that TiO2 is distributed on surface of zeolit nature of Malang. The result of SEM is strengthened with the XRF data from nanocomposite TiO2/zeolite nature of Malang with early degree Ti is from 2,65 % to 46,4 %.

Item Type: Thesis (Undergraduate)
Supervisor: Amalia, Suci and Abtokhi, Ahmad
Keywords: Zeolit Alam Malang; Nanokomposit Tio2/Zeolit Alam; Variasi Hno3; Metode Sol- Gel; Nature Zeolite Of Malang; Nanocomposite Tio2/Zeolite Nature; Variation Of Hno3; Sol-Gel Method
Departement: Fakultas Sains dan Teknologi > Jurusan Kimia
Depositing User: Imam Rohmanu
Date Deposited: 20 Apr 2017 09:31
Last Modified: 20 Apr 2017 09:31
URI: http://etheses.uin-malang.ac.id/id/eprint/6490

Actions (login required)

View Item View Item