Andika, Amalia Savira (2023) Sintesis dan karakterisasi SrTiO3 dengan metode lelehan garam NaCl-KCl terhadap aktivitas antibakteri Staphylococcus aureus. Undergraduate thesis, Universitas Islam Negeri Maulana Malik Ibrahim.
![]() |
Text (Full text)
19630060.pdf - Accepted Version Available under License Creative Commons Attribution Non-commercial No Derivatives. Download (1MB) |
Abstract
Indonesian:
Senyawa perovskit memiliki sifat fotokatalis yang berpotensi digunakan sebagai antibakteri. Penelitian ini bertujuan untuk mengetahui kemampuan senyawa SrTiO3 hasil sintesis metode lelehan garam NaCl-KCl terhadap aktivitas antibakteri Staphylococcus aureus. Uji aktivitas antibakteri menggunakan metode Total Plate Counting (TPC) dengan variasi konsentrasi 2,5; 5; dan 10 mg. Hasil sintesis dikarakterisasi menggunakan instrumen difraksi sinar-X (XRD) yang digunakan untuk mengidentifikasi fasa dan struktur yang terbentuk; instrumen Scanning Electron Microscopy (SEM) yang digunakan untuk mengetahui struktur morfologi dan komposisi unsur serta ukuran partikel; dan instrumen UV-VIS Diffuse Reflectance Spectroscopy (DRS) yang digunakan untuk mengetahui energi celah pita dari material. Difraktogarm sampel menunjukan bahwa senyawa SrTiO3 berhasil disintesis dan didapatkan puncak khas dari SrTiO3 pada 2θ: 22,7; 32,4; 39,9; 46,5; 52,4; 57,9; 68,0; 72,6; 77,3; 81,7; dan 86,2° dan tidak ditemukan adanya pengotor. Morfologi senyawa yang didapatkan morfologi yang tidak sama dan beragam. Didapatkan energi celah pita senyawa SrTiO3 dengan sebesar 3,08 eV. Hasil uji aktivitas antibakteri senyawa SrTiO3 dengan variasi konsentrasi 2,5; 5; dan 10 mg menggunakan cahaya masing- masing sebesar 8,88; 5,34; dan 12,10 CFU/mL dan tanpa cahaya masing-masing sebesar 11,45; 4,73; dan 6,18 CFU/mL menunjukan bahwa senyawa SrTiO3 kurang memiliki potensi sebagai antibakteri yang dapat menghambat pertumbuhan bakteri.
English:
Perovskite compounds possess photocatalytic properties that could potentially be used as antibacterial agents. This study investigated the potential of SrTiO3 compounds synthesized through the NaCl-KCl molten method to act as antibacterial agents against Staphylococcus aureus. To do so, the antibacterial activity of the compounds was tested using the Total Plate Counting (TPC) method at concentrations of 2.5, 5, and 10 mg. The synthesis results were characterized using an X-ray diffraction (XRD) instrument to identify the phase and structure formed, a scanning electron microscopy (SEM) instrument to determine the morphological structure, elemental composition, and particle size, and a UV-VIS diffuse reflectance spectroscopy (DRS) instrument to determine the band gap energy of the material. The results showed that the SrTiO3 compound was successfully synthesized, typical peaks of SrTiO3 were obtained at 2θ: 22.7; 32.4; 39.9; 46.5; 52.4; 57.9; 68.0; 72.6; 77.3; 81.7; 86.2°, and its purity was confirmed with no impurities detected. The morphology of the obtained compounds was different. The band gap energy of the SrTiO3 compound was 3.08 eV. However, the results of the antibacterial activity test of SrTiO3 compounds with concentrations of 2.5, 5, and 10 mg with and without light showed that they had limited potential as antibacterial agents that can inhibit the growth of bacteria. The CFU/mL values were 8.88, 5.34, and 12.10 with light and 11.45, 4.73, and 6.18 without light, respectively.
Arabic:
مركبات البيروفسكايت لها خصائص محفزة ضوئيا يمكن استخدامها كمضادات للبكتيريا. يهدف هذا البحث إلى تحديد قدرة مركبات SrTiO3 من تخليق طريقة ذوبان ملح NaCl-KCl ضد النشاط المضاد للبكتيريا للمكورات العنقودية الذهبية. اختبار النشاط المضاد للبكتيريا باستخدام طريقة العد الكلي للوحة (TPC) مع اختلاف تركيز 2.5 ؛ 5; و 10 ملغ. توصيف نتائج التوليف باستخدام أدوات حيود الأشعة السينية (XRD) المستخدمة لتحديد المراحل والهياكل المتكونة. أداة المجهر الإلكتروني الماسح (SEM) المستخدمة لتحديد التركيب المورفولوجي والتركيب الأولي وكذلك حجم الجسيمات؛ وأدوات التحليل الطيفي للانعكاس المنتشر للأشعة المرئية وفوق البنفسجية (DRS) المستخدمة لتحديد طاقة فجوة النطاق للمواد. أظهرت عينات ديفراكتوجورم أن مركب SrTiO3 تم تصنيعه بنجاح وحصل على قمة نموذجية من SrTiO3 عند θ 2= 22،7؛ 32,4; 39,9; 46,5; 52,4; 57,9; 68,0; 72,6; 77,3; 81,7; و 86.2 درجة ولم يتم العثور على شوائب. مورفولوجية المركبات التي تم الحصول عليها ليست متجانسة وغير موحدة. يتم الحصول على طاقة فجوة النطاق للمركب SrTiO3 بحجم 3.08 فولت. نتائج اختبار النشاط المضاد للبكتيريا لمركبات SrTiO3 مع اختلاف تركيز 2.5؛ 5; و 10 ملغ باستخدام الضوء في 8.88 ؛ 5,34; و 12.10 CFU/mL ولا يوجد ضوء عند 11.45؛ 4,73; و 6.18 CFU/mL وهذا يدل على أن مركب SrTiO3 يفتقر إلى القدرة المضادة للبكتيريا والتي تكون قادرة على تثبيط نمو البكتيريا.
Item Type: | Thesis (Undergraduate) |
---|---|
Supervisor: | Prasetyo, Anton and Fasya, A. Ghanaim |
Keywords: | SrTiO3; Antibakteri; Fotokatalis; Lelehan Garam. SrTiO3; Antibacterial; Photocatalyst; Molten Salt. SrTiO3; مضاد للبكتيريا; محفز ضوئي; ملح مذاب |
Departement: | Fakultas Sains dan Teknologi > Jurusan Kimia |
Depositing User: | Amalia Savira Andika |
Date Deposited: | 13 Mar 2024 10:22 |
Last Modified: | 13 Mar 2024 10:22 |
URI: | http://etheses.uin-malang.ac.id/id/eprint/59802 |
Downloads
Downloads per month over past year
Actions (login required)
![]() |
View Item |