Potensi penyerapan Gelombang Mikro pada Komposit PVC/SiO2/Fe3O4

Umami, Khoirul (2014) Potensi penyerapan Gelombang Mikro pada Komposit PVC/SiO2/Fe3O4. Undergraduate thesis, Universitas Islam Negeri Maulana Malik Ibrahim.

[img] Text (Fulltext)
10640022.pdf - Accepted Version
Restricted to Repository staff only
Available under License Creative Commons Attribution Non-commercial No Derivatives.

Download (4MB) | Request a copy

Abstract

ABSTRAK

Aplikasi teknologi penyerapan gelombang mikro sudah banyak dilakukan, baik dalam bidang telekomunikasi maupun militer. Penelitian ini bertujuan untuk mengetahui sifat dielektrik (permitivitas, resistansi terhadap frekuensi dan impedansi) komposit, mengetahui sifat magnetik, dan mengetahui hasil serapan gelombang mikro. Komposit dibuat dari PVC sebagai matriks, sedangkan SiO2 dan Fe3O4 sebagai filler. Perbandingan komposisi filler pada SiO2 dan Fe3O4 yaitu 1:0 ; 0,2:0,8 ; 0,4:0,6 ; 0,6:0,4 ; 0,2:0,8 ; dan 0:1 (%wt). Hasil sifat dielektrik paling besar terdapat pada sampel dengan tebal 1 mm, dengan nilai impedansi dan permitivitas komposit yang dibuktikan dengan adanya polarisasi Space Charge dan dipolar. Semakin besar frekuensi arus (AC), maka semakin kecil nilai resistansi pada kapasitor tersebut. Kenaikan presentase filler Fe3O4, meningkatkan suseptibilitas magnetik dan hasil serapan gelombang mikro. Hasil pengujian VNA menunjukkan nilai Reflection Loss maksimum terjadi pada variasi komposisi filler Fe3O4 100% sebesar -36,54 dB pada frekuensi 8,5GHz dengan nilai penyerapan sebesar 99,9% dan nilai suseptibilitasnya adalah ≥ 10-6 m3/kg.

ABSTRACT

Applications of microwave absorption technologies has been done, in telecommunications and military field. In this research is determine the dielectric properties (permittivity, resistance to frequency, and impedance) composite, the magnetic properties, and reflectance values. Composite consist on PVC matrix, SiO2 and Fe3O4 fillers. The ratio of filler in SiO2 and Fe3O4 is 1:0; 0,2:0,8; 0,4:0,6; 0,6:0,4; 0,2:0,8; and 0:1 (%wt). The results indicate thickness 1 mm quite high dielectric properties. So, impedance and permittivity value of composite was evidenced by the Space Charge and dipolar polarization. The frequency (AC) increases, there is an decrease in resistance value. The Fe3O4 filler percentage increases as the magnetic susceptibility and reflectance values increases. The results indicate -36,54 dB quite high reflectance values in 8.5 GHz with Fe3O4 filler 100%, absorbance is 99.9%, and susceptibility value is ≥ 10-6 m3/kg.

Item Type: Thesis (Undergraduate)
Supervisor: Hastuti, Erna and Syarifah, Umaiyatus
Contributors:
ContributionNameEmail
UNSPECIFIEDHastuti, ErnaUNSPECIFIED
UNSPECIFIEDSyarifah, UmaiyatusUNSPECIFIED
Keywords: Penyerapan; Gelombang Mikro; Komposit; PVC; SiO2; Fe3O4 Absorption; Microwave; Composite; PVC; SiO2; Fe3O4
Departement: Fakultas Sains dan Teknologi > Jurusan Fisika
Depositing User: Moch. Nanda Indra Lexmana
Date Deposited: 03 May 2023 14:00
Last Modified: 03 May 2023 14:00
URI: http://etheses.uin-malang.ac.id/id/eprint/49376

Downloads

Downloads per month over past year

Actions (login required)

View Item View Item