Hanina, Helwatil (2012) Kajian Adsorpsi Rhodamin B pada Zeolit Alam Termodifikasi. Undergraduate thesis, Universitas Islam Negeri Maulana Malik Ibrahim.
![]() |
Text (Fulltext)
08630055.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Attribution Non-commercial No Derivatives. Download (2MB) | Request a copy |
Abstract
ABSTRAK
Telah dilakukan kajian adsorpsi rhodamin B pada zeolit alam termodifikasi, rhodamin B sebagai adsorbat dan zeolit alam Malang yang dimodifikasi surfaktan CTAB (cetiltrymethilammonium bromide) sebagai adsorben. Zeolit merupakan mineral yang tersusun dari kerangka silika-alumina tetrahedral secara tiga dimensi. Untuk meningkatkan daya adsorpsi terhadap zeolit alam Malang, maka dalam penelitian ini dilakukan modifikasi permukaan zeolit dengan surfaktan CTAB. Penelitian ini bertujuan untuk mengetahui pengaruh lama pengocokan dan konsentrasi CTAB pada proses modifikasi zeolit alam terhadap adsorpsi rhodamin B.
Adsorpsi rhodamin B pada zeolit alam termodifikasi dilakukan dengan cara melakukan variasi lama pengocokan 10, 20, 30, 40, 50 dan 60 menit dan variasi konsentrasi surfaktan CTAB pada proses modifikasi, yaitu 0,25; 0,50; 0,75 dan 1 mM pada pH 2. Karakterisasi yang digunakan meliputi karakterisasi dengan XRD (X-Ray Difraction) untuk mengetahui jenis kristal dari zeolit alam Malang, dan karakterisasi dengan FTIR (Fourier Transform Infra Red) untuk mengetahui keberadaan CTAB pada zeolit alam termodifikasi.
Hasil penelitian menunjukkan bahwa pada variasi lama pengocokan adsorpsi, semakin lama pengocokan dari 10 sampai 60 menit semakin banyak jumlah rhodamin B yang teradsorpsi. Diperoleh lama pengocokan terbaik adsorpsi, yaitu pada menit ke-60 yang mempunyai daya adsorpsi sebesar 9,439 mg/g untuk zeolit alam; 8,954 mg/g untuk zeolit-CTAB 0,25 mM; 7,946 mg/g untuk zeolit-CTAB 0,50 mM; 8,220 mg/g untuk zeolit-CTAB 0,75 mM dan 7,894 mg/g untuk zeolit-CTAB 1 mM. Variasi konsentrasi surfaktan CTAB 0; 0,25; 0,50; 0,75 dan 1 mM pada proses modifikasi zeolit alam, menunjukkan bahwa semakin besar konsentrasi surfaktan CTAB, maka daya adsorpsi dari zeolit alam termodifikasi relatif semakin kecil. Jenis kristal dari zeolit alam Malang yaitu, mordenite dan pita serapan yang menunjukkan bahwa zeolit telah dimodifikasi dengan CTAB adalah pada daerah 2925,110 cm-1 dan 2855,310 cm-1 yang merupakan regangan simetris dan asimetris gugus CH3-R.
ABSTRACT
Has done research about study of adsorption rhodamine B on modified natural zeolite, rhodamine B as the adsorbate and the natural zeolite of Malang are modified by the surfactant CTAB (cetiltrymethilammonium bromide) as an adsorbent. Zeolite is a mineral composed of silica-alumina tetrahedral framework in three dimensions. To enhance the adsorption on natural zeolite Malang, then in this research zeolite surface modification with CTAB surfactant. This study aims to determine the effect of agitation time and concentration of CTAB on the adsorption rhodamine B on modified natural zeolite.
Rhodamine B adsorption on modified natural zeolite by performing a variation of agitation time 10, 20, 30, 40, 50 and 60 minutes and the variation of the concentration of surfactant CTAB in the modification process, 0,25; 0,50; 0,75 and 1 mM in pH 2. Characterization used include characterization by XRD (X- Ray Difraction) to determine the type of crystals of natural zeolite Malang, and characterization by FTIR (Fourier Transform Infra Red) to determine the presence of CTAB on modified natural zeolite.
The results showed that the variation of adsorption agitation time, the longer the agitation, which was from 10 to 60 minutes more the number of rhodamine B adsorbed. Obtained the best long agitation of the adsorption, in the 60 minute having adsorp power of 9,439 mg/g for natural zeolite; 8,954 mg/g for zeolite-CTAB 0,25 mM; 7,946 mg/g for zeolite-CTAB 0,50 mM; 8,220 mg/g for zeolite-CTAB 0,75 mM and 7,894 mg/g for zeolite-1 mM CTAB. Variation of the concentration of surfactant CTAB 0; 0,25; 0,50; 0,75 and 1 mM in the process of modification of natural zeolites, can not find the optimum concentration of surfactant CTAB, but it can only be said that the greater the concentration of the surfactant CTAB, the power of modified natural zeolite adsorp relatively smaller. Types of crystals of natural zeolite mordenite and absorption band indicating that the zeolite has been modified with CTAB is the area of 2925,110 cm-1 and 2855,310 cm-1 which is a vibrations symmetric and asymmetric CH3-R group.
Item Type: | Thesis (Undergraduate) | |||||||||
---|---|---|---|---|---|---|---|---|---|---|
Supervisor: | Prasetyo, Anton and Romaidi, Romaidi | |||||||||
Contributors: |
|
|||||||||
Keywords: | Adsorpsi; Rhodamin B; Zeolit Alam Termodifikasi; Adsorption; Rhodamine B; Modified Natural Zeolite | |||||||||
Departement: | Fakultas Sains dan Teknologi > Jurusan Kimia | |||||||||
Depositing User: | Koko Prasetyo | |||||||||
Date Deposited: | 06 Apr 2023 09:20 | |||||||||
Last Modified: | 06 Apr 2023 09:20 | |||||||||
URI: | http://etheses.uin-malang.ac.id/id/eprint/49235 |
Downloads
Downloads per month over past year
Actions (login required)
![]() |
View Item |