Preparasi, Modifikasi, dan Karakterisasi Katalis Bifungsional Sn-H-Zeolit Alam Malang

Erlina, Nur Okta (2012) Preparasi, Modifikasi, dan Karakterisasi Katalis Bifungsional Sn-H-Zeolit Alam Malang. Undergraduate thesis, Universitas Islam Negeri Maulana Malik Ibrahim.

[img] Text (Fulltext)
08630006.pdf - Accepted Version
Restricted to Repository staff only
Available under License Creative Commons Attribution Non-commercial No Derivatives.

Download (2MB) | Request a copy

Abstract

ABSTRAK

Telah dilakukan preparasi, modifikasi dan karakterisasi katalis Sn-H-Zeolit alam Malang. Zeolit alam diaktivasi dengan menggunakan larutan asam NH4NO3 2 M sehingga dihasilkan H-Zeolit. Logam Sn diimpregnasikan pada sampel H- Zeolit menggunakan variasi konsentrasi SnCl2.2H2O 0,12: 0,24 dan 0,48 M. Metode yang digunakan adalah proses hidrotermal menggunakan suhu 90 °C selama 12 jam, kemudian dikalsinasi pada suhu 500 °C selama 4 jam. Karakterisasi katalis meliputi morfologi permukaan katalis menggunakan SEM- EDAX, analisis kesaman menggunakan adsorpsi ammonia, luas permukaan spesifik katalis menggunakan BET (NOVA-1200) serta kristalinitas katalis menggunakan XRD.

Hasil penelitian menunjukkan bahwa distribusi logam terbaik pada pengemban zeolit adalah pada penggunaan konsentrasi logam SnCl2.2H2O 0,24 M. Nilai keasaman dari hasil variasi terbaik adalah 0,4682 mmol/g, sedangkan luas permukaan spesifiknya adalah sebesar 2,268 m2/g. Dari hasil karakterisasi XRD dapat diketahui bahwa proses modifikasi pada zeolit tidak menyebabkan perubahan struktur dan kristalinitas katalis.

ABSTRACT

Have done preparation, modification and characterization of catalysts Sn-H- natural Zeolite Malang. Natural zeolites were activated by using 2 M NH4NO3 acid solution to produce H-zeolites. Sn metal is impregnationded on H-zeolite samples using concentration variation SnCl2.2H2O 0.12: 0,24 and 0,48 M. The method used is a hydrothermal process using a temperature of 90 °C for 12 hours, and then calcined at a temperature of 500 °C for 4 hours. Characterization of catalysts include catalysts surface morphology using SEM-EDAX, equality analysis using ammonia adsorption, specific surface area of the catalyst using the BET (NOVA-1200) and the crystallinity of the catalysts using XRD.

The results showed that the distribution of the best metal on a zeolite carrier is on the use of metal concentrations SnCl2.2H2O 0,24 M. Acidity values of yield variation is best to 0,4682 mmol/g, while the specific surface area is equal to 2,268 m2/g. From the results of XRD characterization can be seen that the process of modification on zeolite does not cause changes in the structure and crystallinity of the catalyst.

Item Type: Thesis (Undergraduate)
Supervisor: Amalia, Suci and Abtokhi, Ahmad
Contributors:
ContributionNameEmail
UNSPECIFIEDAmalia, SuciUNSPECIFIED
UNSPECIFIEDAbtokhi, AhmadUNSPECIFIED
Keywords: Zeolit alam; Impregnasi; logam SnCl2.2H2O; Natural Zeolites; impregnation; metal SnCl2.2H2O
Departement: Fakultas Sains dan Teknologi > Jurusan Kimia
Depositing User: Koko Prasetyo
Date Deposited: 06 Apr 2023 09:20
Last Modified: 06 Apr 2023 09:20
URI: http://etheses.uin-malang.ac.id/id/eprint/49198

Downloads

Downloads per month over past year

Actions (login required)

View Item View Item