Azmiyani, Ulal (2018) Adsorpsi logam Fe dan Cu menggunakan biosorben batang jagung termodifikasi asam sitrat pada limbah laboratorium UIN Maulana Malik Ibrahim Malang. Undergraduate thesis, Universitas Islam Negeri Maulana Malik Ibrahim.
|
Text (Fulltext)
12630087.pdf - Accepted Version Available under License Creative Commons Attribution Non-commercial No Derivatives. Download (2MB) | Preview |
Abstract
INDONESIA:
Batang jagung mengandung sekitar 40-50% selulosa, 15-29% hemiselulosa, 16-21% lignin yang mengandung gugus-gugus fungsi, hidroksil, karboksil dan fenol yang berpotensi mengikat ion logam. Pada penelitian ini dilakukan aktivasi batang jagung menggunakan HCl 0,1 M dan modifikasi menggunakan asam sitrat untuk mengubah hidroksil membentuk ester yang mempunyai kemampuan lebih tinggi dalam menyerap logam. Hasil aktivasi dikarakterisasi menggunakan XRF dan hasil modifikasi batang jagung menggunakan asam sitrat dianalisis secara kuantitatif dengan titrasi asam basa dan dikarakterisasi gugus fungsi menggunakan FTIR. Hasil modifikasi diaplikasikan pada limbah cair laboratorium kimia. Pengamatan dilakukan pada penurunan konsentrasi logam Fe dan Cu. Adsorpsi logam Fe dan Cu terhadap limbah dianalisis menggunakan AAS.
Hasil karakterisasi pada XRF menunjukkan bahwa kandungan unsur K mengalami penurunan % berat, sedangkan unsur lain seperti Si, Fe, Cu dan P mengalami peningkatan % berat. Hasil penelitian menunjukkan bahwa konsentrasi asam sitrat 2,5 M memberikan nilai konsentrasi gugus asam total (karboksil dan fenol) tertinggi dengan nilai sebesar 2,935 mek/g. Hasil spektra FTIR setelah proses modifikasi menggunakan asam sitrat menunjukkan adanya gugus baru ester (1733-1734 cm-1). Hasil analisis AAS terhadap penurunan logam Fe dan Cu pada limbah laboratorium kimia menggunakan biosorben batang jagung termodifikasi asam sitrat menunjukkan telah terjadi penurunan konsentrasi limbah logam. Penurunan konsentrasi logam Fe terbesar adalah pada biosorben batang jagung termodifikasi asam sitrat 2,5 M, yaitu sebesar 195,375 ppm atau 88,8%. Dan penurunan konsentrasi logan Cu terbesar adalah pada biosorben batang jagung termodifikasi asam sitrat 1,5 M yaitu sebesar 82,775 ppm atau 45,28%.
ENGLISH:
Corn stalks contain about 40-50% cellulose, 15-29% hemicellulose, 16-21% lignin containing functional groups, hydroxyl, carboxyl and phenol which are potentially binding to metal ions. In this study, corn stalk activation using 0.1 M HCl and modification using citric acid to convert hydroxyl form ester has a higher ability to absorb metal. The activation results were characterized using XRF and the result of modification of corn stalk using citric acid was analyzed quantitatively with acid base titration and characterized by functional groups using FTIR. The result of the modification was applied to chemical laboratory liquid waste. Observations were made on decreasing concentrations of Fe and Cu metals. Adsorption of Fe and Cu metals to waste was analyzed using AAS.
The characterization results in XRF showed that the K element content decreased by weight, while other elements such as Si, Fe, Cu and P increased by weight. The results showed that the concentration of citric acid 2.5 M gave the highest concentration of total acid (carboxy and phenol) group with the value of 2,935 mek / g. FTIR spectra results after modification using citric acid showed a new ester group (1733-1734 cm-1). The result of AAS analysis on the decrease of Fe and Cu metals in chemical laboratory wastes using citric acid-modified cornstock biosorben showed that there was a decrease of metal waste concentration. The greatest decrease in Fe metal concentration was in the modified citrate corn biosorbent of 2.5 M, which was 195.375 ppm or 88.8%. And the biggest decrease of Cu logan concentration was on the corn stem biosorbent of citric acid 1.5 M that is equal to 82,775 ppm or 45,28%.
Item Type: | Thesis (Undergraduate) | |||||||||
---|---|---|---|---|---|---|---|---|---|---|
Supervisor: | Yulianti, Eny and Imamudin, Mochamad | |||||||||
Contributors: |
|
|||||||||
Keywords: | batang jagung; asam sitrat; gugus fungsi; corn stalk; citric acid; funcional group | |||||||||
Departement: | Fakultas Sains dan Teknologi > Jurusan Kimia | |||||||||
Depositing User: | Heni Kurnia Ningsih | |||||||||
Date Deposited: | 11 Mar 2019 14:52 | |||||||||
Last Modified: | 12 Jun 2023 09:08 | |||||||||
URI: | http://etheses.uin-malang.ac.id/id/eprint/13364 |